Home > Standard > 1.4120, DIN X20CrMo13 standard

1.4120, DIN X20CrMo13

1.4120, DIN X20CrMo13 standard Download, We provide the main countries around the ISO standard download, including: AISI(US),UNS(US),SAE(US),ASTM(US),AMS(US),ASME(US),MIL(US),FED(US),DIN(DEU),JIS(JPN),AFNOR(FR),B.S.(UK),SS(SWE),UNI(ITA).

Production specification

Round bar standard Download
Square-shape steel standard Download
Plate steel standard Download
Billet standard Download
Flat bar standard Download
wire standard Download
tube standard Download
pipe standard Download
Forging standard Download
casting standard Download
sheet standard Download
round bar standard Download
coil standard Download
Bar stock standard Download
profiled bar standard Download

Click on the download 1.4120, DIN X20CrMo13 standard

1.4120, DIN X20Cr Mo13

Designation by Standards

Brand Name	LH No.	Mat. No.	DIN	EN	AISI
PK320	320	1.4120	X20Cr Mo13	-	-

Chemical Composition (in weight %)

C	Si	Mn	Cr	Mo	Ni	V	W	Others
2.05	0.25	0.30	11.50	-	-	-	-	-

Description
PK320 is stainless, heat resistant steel up to temperature of 550^oC. Steel is resistant to water with a low chlorine content in fine-machined or, better still, polished condition.

Applications
Owing to its greater high-temperature strength and corrosion resistance - resulting from the addition of molybdenum - PK320 is used for shafts and blades in water and steam turbine systems. One special field of application is for bedknives in the cellulose industry.

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [10³ x N/mm²]: Approx. 210
Density [g/cm³]: 7.7
Thermal conductivity [W/m.K]: 25.0
Electric resistivity [Ohm mm²/m]: 0.60
Specific heat capacity[J/g.K]: 0.43
Magnetisable: Yes

Coefficient of Linear Thermal Expansion 10^-6 ^oC^-1

20-100^oC	20-200^oC	20-300^oC	20-400^oC	20-500^oC	20-600^oC	20-700^oC
11.7	12.0	12.4	12.9	13.3	13.6	14.0

Annealing
Heat to 750-850^oC, cool slowly in furnace. Tensile strength is max. 770 N/mm². Structure is ferrite with spherical carbides.

Quenching
Harden from a temperature of 950-1000^oC followed by oil quenching.

Tempering
Tempering temperature: 650-750^oC, them air cooling. Structure is transformation structure with ferrite.

Mechanical properties at at ambient temperature
Condition: Quenched, d<=160 mm
Hardness: max. 220-280 HB
0.2 % proof stress: 550 N/mm²
Tensile strength: 750-900 N/mm²
Elongation: 14%
Charpy notch (ISO-V): 28 J (Longit.)

0.2 % Proof Stress in N/mm² vs. Tempering Temperature in ^oC

100^oC	150^oC	200^oC	250^oC	300^oC	350^oC	400^oC
520	510	500	490	480	450	410

Forging
Hot forming temperature: 1100-800^oC, slow cooling.

Machinability
Metal cutting machining is teh same as that for special engineering steel grades of corresponding strength.

Welding
Only limted weldability using the manual arc, resistance and TIG welding process, as hardening occurs in the heat-affected zone. Filler material is Themanit or 1520.

Note: PK320 is primarily supplied in quenched and tempered condition. It can be set to other strength ranges. Is must be borne in mind in this context that the temperature range between 420 and 520 must be avoided owing to embrittlemnent at 475^oC.

Note: Optimum corrosion resistance is only ensured with a bright metallic surface.

Prev:1.4021, DIN X20Cr13, AISI ~410
Next:1.4913*, DIN X19CrMoVNbN11-1

Click on the download 1.4120, DIN X20CrMo13 standard

1.4120, DIN X20CrMo13

Production specification