Home > Standard > 1.4006, DIN X15Cr13, AISI 410 standard

1.4006, DIN X15Cr13, AISI 410

1.4006, DIN X15Cr13, AISI 410 standard Download, We provide the main countries around the ISO standard download, including: AISI(US),UNS(US),SAE(US),ASTM(US),AMS(US),ASME(US),MIL(US),FED(US),DIN(DEU),JIS(JPN),AFNOR(FR),B.S.(UK),SS(SWE),UNI(ITA).

Production specification

Round bar standard Download
Square-shape steel standard Download
Plate steel standard Download
Billet standard Download
Flat bar standard Download
wire standard Download
tube standard Download
pipe standard Download
Forging standard Download
casting standard Download
sheet standard Download
round bar standard Download
coil standard Download
Bar stock standard Download
profiled bar standard Download

 1.4006, DIN X15Cr13, AISI 410

Designation by Standards

 

Brand Name LH No. Mat. No. DIN EN AISI
PK2 904 1.4006 X15Cr13 X15Cr13 410



Chemical Composition (in weight %)

C Si Mn Cr Mo Ni V W Others
0.14 max. 1.00 max. 1.00 13.00 - - - - -



Description
PK2 is the basic martensitic stainless which will attain high mechanical properties after heat treatment. It has good impact strength, corrosion and scaling resistance up to 649oC.

Applications
Cutlery, steam and gas turbine blades and buckets, bushings, valve components, fasteners, screens and kitchen utensils.

Physical properties (avarage values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 216
Density [g/cm3]: 7.73
Thermal conductivity [W/m.K]: 30.0
Electric resistivity [Ohm mm2/m]: 0.60
Specific heat capacity[J/g.K]: 0.46

Coefficient of Linear Thermal Expansion 10-6 oC-1

20-100oC 20-200oC 20-300oC 20-400oC 20-500oC
10.5 11.0 11.5 12.0 12.0



Soft Annealing
Heat to 750-800oC, cool slowly in furnace.

Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to approx. 650oC, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

Hardening
Harden from a temperature of 980-1030oC followed by oil or air quenching.

Tempering
Tempering temperature: 700-750oC

Mechanical properties at at ambient temperature
Condition: annealed
Hardness: max. 225 HB
Tensile strength: max. 720 N/mm2

Condition: annealed and hardened
Hardness: 180-230 HB
0.2 % proof stress: 450 N/mm2
Tensile strength: 650-800 N/mm2
Elongation: min. 14%
Impact strength: 30 J

0.2% Proof Stress in N/mm2 vs. Temperature in oC

50oC 100oC 150oC 200oC 250oC 300oC 350oC 400oC
430 420 410 400 382 365 335 305


Forging
Hot forming temperature: 1100-800oC.

Machinability
Tough, draggy chips with heavy build-up. While this alloy can be machined in the annealed condition, it tends to perform better in the cold drawn or heat treated condition.

Corrosion Resistance
Not known for its exceptional corrosion resistance, this alloy will stand up well to mild atmospheric conditions and fresh waters.

Welding
Most common methods of welding can be successfully employed with this alloy. To reduce the chance of cracking, it is advisable to preheat the workpiece to 177-204oC. Post-weld annealing is recommended to reattain maximum ductility.

Cold working
Readily cold formed using most of the common practices.

Related hot word search:1.4006 DIN X15Cr13 AISI 410 1.4006, DIN X15Cr13, AISI 410 round bar,1.4006, DIN X15Cr13, AISI 410 forging,1.4006, DIN X15Cr13, AISI 410 sheet,1.4006, DIN X15Cr13, AISI 410 coil,1.4006, DIN X15Cr13, AISI 410 flat bar,1.4006, DIN X15Cr13, AISI 410 pipe,1.4006, DIN X15Cr13, AISI 410 Lrregular